menusearch
stacommercial.com

Construction materials

Sepehr Tejarat Amir (S.T.A) Company was established in the year of 2009 with the aim of doing fair and scientific trading.

(0)
(0)
Construction materials

Cement packaging 

1- 50 kg polypropylene packets; 

2- 1.5 ton jumbo bag in two forms i.e. jumbo packet and jumbo bulk bags; Jumbo bags have one nylon layer (laminate); 

3- Bulk 

 

Certificates 

- ISO 9001:2015 

- ISO14001:2015 

- OHSAS 18001:2007 

- ISO50001:2011 

- CE Mark 

- GOST-R 

 

The ProductsPage Break 

 

Product 

Portland Cement Type 1-325 ( M 400) 

Standard 

ISIRI 389,EN197-1,GOST 10178 

Physical Properties 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 Setting Time (Vicat ,Initial) 

 170 

 Min 45 

 Min 45 

 Minute 

 Setting Time (Vicat ,Final) 

 3/5 

 Max 6:00 

 Max 10:00 

 hr 

 Expansion (Autoclave) 

 0/1 

 Max 0.8 

 _ 

 % 

 Specific Surface Area (Blaine) 

 3250 

 Min 2800 

 Min 2800 

 cm2/gr 

 Residue on 90m Sieve 

 1 

  

  

 % 

 Compressive Strengh (1 day) 

  

  

  

 kg/cm2 

 Compressive Strengh (2 days) 

  

  

  

 kg/cm2 

 Compressive Strengh (3 days) 

 270 

 Min 120 

  

 kg/cm2 

 Compressive Strengh (7 days) 

 370 

 Min 200 

  

 kg/cm2 

Compressive Sterngh (28 days) 

 480 

 Min 325Max525 

 Min400 

 kg/cm2 

 

Chemical Analysis 

Factory test result 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 SiO2 

 21/18 

 ... 

  

 % 

 Al2O3 

 5/24 

  ... 

  

%  

 Fe2O3 

 3/55 

  ... 

  

%  

 CaO 

 63.56 

  ... 

  

%  

 MgO 

 1.79 

 Max 5.00 

 Max 5.00 

%  

 SO3 

 2.33 

 Max 3.00 

 Max 3.50 

%  

 Insoluble Residue 

 0.42 

 Max 0.75 

  

%  

 Loss On Ignation 

 1.30 

 Max 3.00 

  

%  

 Free CaO 

 1.4 

  

  

%  

K2O 

 0.5 

  

  

%  

Na2O 

 0/35 

  

  

%  

Modulus 

Factory test result 

Standard ( ISIRI - 389) 

GOST 10178 

Unit 

 Lime Saturation Factor (LSF) 

 91/35 

  

  

 % 

 Silica Modulus (SM) 

 2/41 

  

  

  

 Alomina Modulus (AM) 

 1/48 

  

  

  

 

Mineralogical Composition 

Factory test result 

Standard ( ISIRI - 389) 

GOST 10178 

Unit 

 C3S 

 50/92 

  

  

 % 

 C2S 

 22/59 

  

  

%  

 C3A 

 7/89 

  

  

%  

 C4AF 

 10/79 

  

  

%  

 

Product 

Portland Cement Type 1-425 ( M400) 

Standard 

ISIRI 389,EN197-1,GOST 10178 

Physical Properties 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 Setting Time (Vicat ,Initial) 

  175 

 Min 45 

 Min 45 

 Minute 

 Setting Time (Vicat ,Final) 

 3/58 

 Max 6:00 

 Max 10:00 

 hr 

 Expansion (Autoclave) 

 0/1 

 Max 0.8 

 … 

 % 

 Specific Surface Area (Blaine) 

 3300 

 Min 2800 

 Min 2800 

 cm2/gr 

 Residue on 90m Sieve 

 1 

  

 80mMax15 

 % 

 Compressive Strengh (1 day) 

  

  

  

 kg/cm2 

 Compressive Strengh (2 days) 

190  

 Min100 

  

 kg/cm2 

 Compressive Strengh (3 days) 

  

  

  

 kg/cm2 

 Compressive Strengh (7 days) 

  

  

  

 kg/cm2 

Compressive Sterngh (28 days) 

 505 

 Min 425Max625 

 Min400 

 kg/cm2 

 

Chemical Analysis 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 SiO2 

 20/7 

  

  

 Al2O3 

 5/3 

  

  

 Fe2O3 

 3/65 

  

  

 CaO 

 63 

  

  

 MgO 

 1.9 

 Max 5.00 

 Max 5.00 

 SO3 

 2.55 

 Max 3.00 

 Max 3.50 

 Insoluble Residue 

 0.4 

 Max 0.75 

  

 Loss On Ignation 

 2.1 

 Max 3.00 

  

 Free CaO 

 1.2 

  

  

K2O 

 0.6 

  

  

 % 

Na2O 

 0/35 

  

  

 % 

 

Product 

Portland Cement Type 1-525 ( M 500) 

Standard 

ISIRI 389,EN197-1,GOST 10178 

Physical Properties 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 Setting Time (Vicat ,Initial) 

 180 

 Min 45 

 Min 45 

 Minute 

 Setting Time (Vicat ,Final) 

 3/7 

 Max 6:00 

 Max 10:00 

 hr 

 Expansion (Autoclave) 

 0/12 

 Max 0.8 

 Max 0.8 

 % 

 Specific Surface Area (Blaine) 

 3150 

 Min 2800 

 Min 2800 

 cm2/gr 

 Residue on 90m Sieve 

 1 

  

 80m.Max15 

 % 

 Compressive Strengh (1 day) 

  

  

  

 kg/cm2 

 Compressive Strengh (2 days) 

 220 

 Min 200 

  

 kg/cm2 

 Compressive Strengh (3 days) 

  

  

  

 kg/cm2 

 Compressive Strengh (7 days) 

  

  

  

 kg/cm2 

Compressive Strengh (28 days) 

 530 

 Min 525 

 Min500 

 kg/cm2 

 

Chemical Analysis 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 SiO2 

 20/85 

  

  

 Al2O3 

 5/15 

  

  

%  

 Fe2O3 

 3/4 

  

  

%  

 CaO 

 63.7 

  

  

%  

 MgO 

 1.7 

 Max 5.00 

 Max 5.00 

 % 

 SO3 

 2.55 

 Max 3.00 

 Max 3.50 

%  

 Insoluble Residue 

 0.35 

 Max 0.75 

  

%  

 Loss On Ignation 

 1.5 

 Max 3.00 

  

%  

 Free CaO 

 1.3 

  

  

%  

 K2O 

 0.55 

  

  

%  

Na2O 

 0/35 

  

  

  

Modulus 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 Lime Saturation Factor (LSF) 

 92/87 

  

  

 % 

 Silica Modulus (SM) 

 2/44 

  

  

  

 Alomina Modulus (AM) 

 1/51 

  

  

  

 

Mineralogical Composition 

Factory test result 

Standard (ISIRI-389) 

GOST 10178 

Unit 

 C3S 

 54/2 

  

  

 % 

 C2S 

 19/19 

  

  

 % 

 C3A 

 7/9 

  

  

%  

C4AF 

 10/34 

  

  

 

Product 

Portland Cement Type 2 ( M 500) 

Standard 

ISIRI 389,EN197-1,GOST 10178 

Physical Properties 

Factory test result 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 Setting Time (Vicat ,Initial) 

 170 

 Min 45 

 Min 45 

 Minute 

Setting Time (Vicat ,Final) 

 3/5 

 Max 6:00 

 Max 10:00 

 hr 

Expansion (Autoclave) 

 0/1 

 Max 0.8 

 Max 0.8 

 % 

Specific Surface Area (Blaine) 

 3250 

 Min 2800 

 Min 2800 

 cm2/gr 

Residue on 90m Sieve 

 1 

  

  

 % 

Compressive Strengh (1 day) 

  

  

  

 kg/cm2 

Compressive Strengh (2 days) 

  

  

  

 kg/cm2 

Compressive Strengh (3 days) 

 270 

 Min 100 

  

 kg/cm2 

Compressive Strengh (7 days) 

 395 

 Min 175 

  

 kg/cm2 

Compressive Strengh (28 days) 

 505 

 Min315 

Min500 

 kg/cm2 

 

Chemical Analysis 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 SiO2 

 20/8 

 Min 20.00 

  

 % 

 Al2O3 

 5/2 

 Max 6.00 

  

%  

 Fe2O3 

 3/65 

 Max 6.00 

  

%  

 CaO 

 63.3 

 …… 

  

%  

 MgO 

 1.8 

 Max 5.00 

 Max 5.00 

%  

SO3 

 2.5 

 Max 3.00 

 Max 3.50 

 % 

Insoluble Residue 

 0.3 

 Max 0.75 

  

%  

Loss On Ignation 

 2.1 

 Max 3.00 

  

%  

Free CaO 

 1.2 

  

  

%  

K2O 

 0.55 

  

  

 % 

Na2O 

 0/3 

  

  

%  

Modulus 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 Lime Saturation Factor (LSF) 

 92/21 

  

  

  

 Silica Modulus (SM) 

 2/35 

  

  

  

 Alomina Modulus (AM) 

 1/42 

  

  

  

 

Mineralogical Composition 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 C3S 

 51/43 

  

  

 % 

 C2S 

 20/98 

  

  

%  

 C3A 

 7/65 

 Max 8.00 

  

%  

C4AF 

 11/07 

  

  

%  

Product 

Portland Cement Type 2 ( M 400) 

Standard 

ISIRI 389,EN197-1,GOST 10178 

 

Physical Properties 

Factory test result 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 Setting Time (Vicat ,Initial) 

 175 

 Min 45 

 Min 45 

 Minute 

Setting Time (Vicat ,Final) 

 3/4 

 Max 6:00 

 Max 10:00 

 hr 

Expansion (Autoclave) 

 0/1 

 Max 0.8 

  

 % 

Specific Surface Area (Blaine) 

 3150 

 Min 2800 

  

 cm2/gr 

Residue on 90m Sieve 

 1 

  

  

 % 

Compressive Strengh (1 day) 

  

  

  

 kg/cm2 

Compressive Strengh (2 days) 

  

  

  

 kg/cm2 

Compressive Strengh (3 days) 

 250 

 Min 100 

  

 kg/cm2 

Compressive Strengh (7 days) 

 375 

 Min 175 

  

 kg/cm2 

Compressive Strengh (28 days) 

 490 

 Min400 

 Min 315 

 kg/cm2 

Chemical Analysis 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 SiO2 

 20/75 

 Min 20.00 

  

 % 

 Al2O3 

 5/21 

 Max 6.00 

  

%  

 Fe2O3 

 3/64 

 Max 6.00 

  

%  

 CaO 

 63.05 

 …… 

  

%  

 MgO 

 1.8 

 Max 5.00 

 Max 5.00 

%  

SO3 

 2.6 

 Max 3.00 

 Max 3.50 

 % 

Insoluble Residue 

 0.34 

 Max 0.75 

  

%  

Loss On Ignation 

 1.98 

 Max 3.00 

  

%  

Free CaO 

 1.2 

  

  

%  

K2O 

 0.50 

  

  

 % 

Na2O 

 0/3 

  

  

%  

 

Modulus 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 Lime Saturation Factor (LSF) 

 91/92 

  

  

  

 Silica Modulus (SM) 

 2/34 

  

  

  

 Alomina Modulus (AM) 

 1/43 

  

  

  

Mineralogical Composition 

Factory test resul 

Standard (ISIRI - 389) 

GOST 10178 

Unit 

 C3S 

 51/43 

  

  

 % 

 C2S 

 20/98 

  

  

%  

 C3A 

 7/65 

 Max 8.00 

  

%  

C4AF 

 11/07 

  

  

%